Coating · zinc flake
Geomet 500
A chromium-free zinc-aluminium flake coating with an integral lubricant. Applied without electrolysis, so it suits high-strength fasteners. Friction coefficient 0.15 ± 0.03 without a separate topcoat.
Sprechen Sie mit Terry · Sales Engineer
Was es ist
How Geomet 500 protects the joint.
01Zinc flake, not platingZinc and aluminium flakes in an inorganic binder, applied by dip-spin or spray and cured. No electrolysis is involved.
02Integral lubricantThe lubricant is built in, giving a friction coefficient of 0.15 ± 0.03 without a separate topcoat.
03Chromium-freeNo hexavalent chromium and no cadmium.
Applications
Where we use it.
01High-strength fastenersBolts and screws where electroplating would bring a hydrogen-embrittlement risk.
02Automotive and railWidely specified by vehicle and rail manufacturers.
03Thin, uniform protectionParts where hot-dip galvanizing is too thick for the thread.
Layer thickness
Thickness, fit and threads.
Layer thickness
> 24 / > 36g/m²
Zinc flake thickness is specified as coating weight. Grade A (> 24 g/m²) reaches > 720 h, grade B (> 36 g/m²) > 1.000 h to red rust in salt spray (ISO 9227 / ASTM B117).
| Güte | Coating weight | Red rust, salt spray |
|---|---|---|
| A | > 24 g/m² | > 720 h |
| B | > 36 g/m² | > 1.000 h |
How it is applied
From bare steel to coated part.
01ReinigenBare steel, free of oil, scale and rust.
02Dip-spin or spraySmall parts in bulk by dip-spin, large parts by spray.
03CureOven cure of the binder.
04CheckCoating weight and friction checked against the specification.
FAQ
Questions we get about Geomet 500.
- Is there a hydrogen-embrittlement risk?
- Zinc flake is applied without electrolysis, which avoids the hydrogen pickup of electroplating – the reason it is used on high-strength fasteners.
- Why coating weight and not µm?
- For zinc flake the protection depends on the amount of zinc, so specifications give g/m².
- Do I need a topcoat?
- Not for lubrication: Geomet 500 has an integral lubricant and reaches 0.15 ± 0.03 without a topcoat.
- Which standard applies?
- ISO 10683 for zinc flake coatings on threaded fasteners.
Next step
Quote, compare or ask.
Reviewed October 2026 by HBS Solutions. Based on NOF Metal Coatings Geomet 500 data and ISO 10683. Corrosion results always belong to a complete system (pretreatment, coating, thickness) – ask us for the data sheet of the system you order.
Other coatings
Compare with another coating.
TAKECOAT-1000Fluorocarbon polymer, 2 layersXylan 1070PTFE dry film, solvent-borneXylan 1424PTFE dry film, waterborneXylan 1427PTFE, extra corrosion protectionHot-dip galvanizedISO 10684 · min 50 µm averageZinc platedElectroplated zinc · ISO 4042SherardizedZinc diffusion · ISO 17668All coatingsCompare them side by side
ANGEBOT INNERHALB VON 24 STUNDEN
Senden Sie uns Ihre Stückliste.
Bestätigung am selben Tag. Ein vollständiges Angebot innerhalb von 24 Stunden.
ANGEBOT ANFORDERN →
IHR ANSPRECHPARTNERSprechen Sie mit TerrySales Engineer01E-Mailsales@hbssolutions.nl02WhatsAppChatten Sie mit unseren Ingenieuren
03Rufen Sie mich zurückHinterlassen Sie Ihre Nummer – Terry ruft Sie an