A2 or A4 stainless – and when duplex?
A2 (type 304) is fine indoors and in mildly corrosive conditions. Choose A4 (type 316, with 2–3 % molybdenum) wherever chlorides are present: coast, splash zones, chemicals and cleaning agents. For permanent immersion in seawater or hot chlorides, move up to duplex or super duplex.
Spreek Terry · Sales Engineer
Short answer
- A2 – 18 % Cr, 8 % Ni. Indoor, dry, food-grade without chlorides.
- A4 – adds molybdenum. Coastal, chemical, cleanroom and offshore topsides.
- Duplex / super duplex – for submerged and hot-chloride service.
- Strength: property class 50, 70 or 80 – the number is the tensile strength ÷ 10 MPa.
Comparison
A2 versus A4.
| A2 | A4 | |
|---|---|---|
| Comparable steel | Type 304 | Type 316 |
| Chromium | 18–20 % | 16–18 % |
| Nickel | 8–11 % | 10–14 % |
| Molybdenum | – | 2–3 % |
| PREN (Cr + 3.3 × Mo, from composition) | approx. 18–20 | approx. 23–28 |
| Chlorides (sea air, salt, de-icing, chemicals) | Not recommended – pitting | Suitable for most exposures |
| Typical use | Indoor, machinery, dry outdoor | Coastal, offshore topsides, chemical, pharma, cleanroom |
Strength
Property classes to ISO 3506-1.
The same for A2 and A4. Classes 70 and 80 are cold worked and available in smaller diameters; ask us for large sizes.
| Property class | Min. tensile strength Rm | Min. 0.2 % proof stress Rp0.2 | Condition |
|---|---|---|---|
| 50 | 500 MPa | 210 MPa | Soft – as machined or hot formed |
| 70 | 700 MPa | 450 MPa | Cold worked – the standard for stainless bolts |
| 80 | 800 MPa | 600 MPa | Highly cold worked – highest strength |
Beyond A4
When 316 is not enough.
- 01Duplex (UNS S31803, F51)Much higher strength than 316 and better resistance to pitting and stress corrosion cracking. For offshore, seawater-cooled and chloride-rich process service.
- 02Super duplex (F53 / UNS S32750, F55 / UNS S32760)Higher chromium, molybdenum and nitrogen again – the usual choice for submerged seawater service.
- 03Nickel alloys (625, 825, 925)For hot acids, sour wells and the most aggressive media. We supply header plugs and specials in these alloys.
- 04A1 – free-machiningContains sulphur for machinability, which lowers corrosion resistance. Not offered with EPK cleanroom treatment.
FAQ
Questions we get every week.
- Is A4 the same as 316?
- A4 is the ISO 3506 steel group that covers 316-type stainless (molybdenum-alloyed austenitic steel). In daily use the names are interchangeable; the certificate shows the actual grade.
- Are stainless bolts magnetic?
- Annealed A2 and A4 are practically non-magnetic. Cold working, as for class 70 and 80, can make them slightly magnetic. That says nothing about the quality.
- Can I put stainless bolts in galvanized steel?
- Yes in most atmospheres: the stainless bolt is small compared to the zinc surface, so contact corrosion stays limited. In wet or immersed conditions, insulate.
- Why do my stainless bolts seize?
- Galling – stainless on stainless cold-welds under load. Use an anti-seize lubricant, tighten more slowly, or choose a coated nut.
- Which stainless for cleanrooms?
- A2 or A4 with EPK treatment: electropolished, Kolsterised, cleaned to Grade 2 or 4 and vacuum-packed. See our cleanroom page.
- What does A4-80 mean?
- Steel group A4 (316-type), property class 80: at least 800 MPa tensile strength.
Next step
Configure, download or ask.
Reviewed October 2026 by HBS Solutions. Based on ISO 3506-1, ASTM A193 (B8, B8M) and published composition data. Values are minimums from the standard; always check the edition and options named in your project specification.
More guides
Other questions engineers ask us.
OFFERTE BINNEN 24 UUR
Stuur ons uw onderdelenlijst.
Bevestiging op dezelfde dag. Een complete offerte binnen 24 uur.
OFFERTE AANVRAGEN →
UW CONTACTPERSOONSpreek TerrySales Engineer01E-mailsales@hbssolutions.nl02WhatsAppChat met onze engineers
03Bel mij terugLaat uw nummer achter – Terry belt u